High Speed Burnt Titanium PETG

Eryone High Speed Burnt Titanium PETG 3D Printing Filament is a material that

surpasses traditional PLA-based combustion titanium filaments. While maintaining high-

speed printing performance (up to 600mm/s), it delivers exceptional toughness and

significantly enhanced resistance to brittle fracture. Its optimized melt flowability ensures

precise molding, producing a delicate metallic-textured surface with unique granular patterns.

The printed parts exhibit strong interlayer adhesion and excellent impact resistance,

effectively mitigating the risk of cracking. Featuring a light-responsive color-shifting effect,

the finished products display an iridescent gradient under different viewing angles, adding a

dynamic visual dimension to creative designs. Combining high strength with artistic

expressiveness, this material is an ideal choice for premium innovative applications.

Part I:Suggests Printing Parameters

Parameter	Set up
Nozzle temperature	230-250 ℃
Bed temperature	75-80℃
Bed materia	glass, PEI, spring steel plate
Bottom printing temperature	230-250 ℃
Sealed printing	enclosed printing/open printing
Printing speed	30-600mm/s
Drying conditions	65℃, 12h

Part II: Physical Properties of Materials

Property	Testing Method	Unit	Typical Value
Density(g/cm³ at 21.5 ° C）	ASTM D792 (ISO 1183, GB/T 1033)	g/cm³	1.25
Vicat Softening Temperature(° C)	ASTM D1525 (ISO 306 GB/T 1633)	℃	78
Heat distortion temperature(° C)	ASTM D648 1.8MPa 0.45MPa	℃	67
Glass transition temperature (° C)	DSC, 10 ° C/min	℃	68
Melt Index(g/10 min)	220 ° C, 10kg 240 ° C, 2.16 kg	g/10min	18±2

Part III: Mechanical Properties of Printed Samples

Property	Test conditions	Test standards	unit	Typical Value
Tensile strength X-Y	50mm/min	GB/T 1040.4	MPa	45.7
Elastic modulus X-Y	50mm/min	GB/T 1040.1-2006	MPa	1301.9
Elongation at break X-Y	50mm/min	GB/T 1040.4	%	2.7
Tensile strength X-Z	50mm/min	GB/T 1843	MPa	31.7
Elastic modulus X-Z	50mm/min	GB/T 1040.1-2006	MPa	1022.5
5Elongation at break X-Z	50mm/min	GB/T 1040.4	%	2.1
Bending strength	2mm/min	GB/T 9341	MPa	70.2
Bending modulus	2mm/min	GB/T 9341	MPa	1953.2
Charpy Impact strenght	2.75J	GB/T 1843	kJ/m2	2.4

Note: All splines are printed under the following conditions: printing temperature=240 ° C, printing speed=80mm/s, base plate 60° C, filling=100%, nozzle diameter=0.4mm

PETG High-Speed All

PETG High-Speed Filament - 1.75mm±0.03mm (1kg)

PETG High Speed Burnt Titanium Filament- 1.75mm±0.03mm (1kg)

PETG High-Speed Translucent Gradient Multi-Color Filament - 1.75mm±0.03mm (1kg)

PETG High-Speed Translucent Filament - 1.75mm±0.03mm (1kg)