Injection Alloy Filament

The ERYONE Alloy Filament is a high-performance composite material made from a

combination of PC and ABS. It offers excellent heat resistance, high toughness, low odor, impact

resistance, and printing stability, with a heated bed temperature requirement of only 70°C and a

tensile strength of approximately 23MPa. Its high precision and low warping characteristics make

it ideal for printing high-strength mechanical parts such as gears and screws, particularly suitable

for functional part manufacturing in high-temperature environments. It is a high-quality 3D

printing material that balances performance and ease of use.

Part I:Suggests Printing Parameters

Parameter	Set up
Nozzle temperature	240-260 ℃
Bed temperature	70-80℃
Bed materia	glass, PEI, spring steel plate
Bottom printing temperature	250-260 ℃
Sealed printing	Supports open printing; better results with enclosure.
Printing speed	30-300mm/s
Drying conditions	70-80℃, 12h

Part II: Physical Properties of Materials

Property	Testing Method	Unit	Typical Value
Density(g/cm³ at 21.5 ° C）	ASTM D792 (ISO 1183, GB/T 1033)	g/cm³	1.05-1.11
Water absorption rate	ASTM D750	%	<0.7
Heat distortion temperature(° C)	ASTM D648 1.8MPa 0.45MPa	℃	65-67
Melt Index(g/10 min)	220 ° C, 10kg 240 ° C, 2.16 kg	g/10min	17-23

Part III: Mechanical Properties of Printed Samples

Property	Test conditions	Test standards	unit	Typical Value
Tensile strength X-Y	50mm/min	GB/T 1040.4	MPa	37.2
Elastic modulus X-Y	50mm/min	GB/T 1040.1-2006	MPa	1532.9
Elongation at break X-Y	50mm/min	GB/T 1040.4	MPa	4.5
Tensile strength X-Z	50mm/min	GB/T 1843	MPa	22.3
Elastic modulus X-Z	50mm/min	GB/T 1040.1-2006	MPa	1375.3
Elongation at break X-Z	50mm/min	GB/T 1040.4	%	3.2
Bending strength	2mm/min	GB/T 9341	MPa	52.8
Bending modulus	2mm/min	GB/T 9341	MPa	1857.1
Charpy Impact strenght	2.75J	GB/T 1843	kJ/m2	14.3

Note: All splines are printed under the following conditions: printing temperature=260 ° C, printing speed=80mm/s, base plate 70° C, filling=100%, nozzle diameter=0.4mm

ABS-PC Alloy Material

ABS-PC Alloy Material Filament - 1.75mm±0.03mm (1kg)